Programming Fracture Resistance in Metamaterials through Elastic Instability Design
Mechanical metamaterials promise tougher, lighter materials—but designing them has been slow because fracture is governed by mechanisms that span many length scales, from atomistic inelasticity to crack propagation through complex architectures. Traditional lattice